RESEARCH ARTICLE

Flexural Strength and Morphological Characteristics of Resin-modified Glass-ionomer Containing Bioactive Glass

Sayed Mostafa Mousavinasab, Maryam Khoroushi, Fateme Keshani, Shirin Hashemi

Citation Information : Mousavinasab SM, Khoroushi M, Keshani F, Hashemi S. Flexural Strength and Morphological Characteristics of Resin-modified Glass-ionomer Containing Bioactive Glass. J Contemp Dent Pract 2011; 12 (1):41-46.

DOI: 10.5005/jp-journals-10024-1008

Published Online: 01-02-2011

Copyright Statement:  Copyright © 2011; Jaypee Brothers Medical Publishers (P) Ltd.


Abstract

Introduction

Recent advances in dental materials have led to the production of smart materials. Recently, addition of bioactive materials to glass-ionomer cements has resulted in new capabilities beyond the beneficial effects of fluoride release. This in vitro study compared the flexural strengths (FS) of a resin-modified glass-ionomer containing bioactive glass (RMGIBAG) with that of a commonly used resin-modified glass-ionomer (RMGI).

Methods and materials

A total of forty RMGI and RMGI-BAG bars (20 × 4 × 4 mm) were prepared in stainless steel molds. Each of the RMGI and RMGI-BAG bars was set for FS test. FS values of the specimens were measured using three-point bending test at a crosshead speed of 0.5 mm/min. The surface changes and the amounts of elements on the materials’ surfaces were also evaluated by SEM/EDS analyses. Data were analyzed using SPSS 11.5 and t-test (a = 0.05).

Results

The means ± SD in the study groups were 61.46 ± 22.52 and 39.90 ± 9.11 MPa respectively. There were significant differences between FS of the two study groups (p = 0.003).

Conclusion

While adding 20 wt% of BAG to the RMGI powder evaluated in this study decreases FS of the material significantly, the mean value of FS is in the acceptable range of the reported FS values for conventional GIs and RMGIs that are commercially available for clinical use.

Clinical significance

While flexural strength of RMGI decreases subsequent to addition of bioactive glass, it is still clinically acceptable considering the flexural strength values reported for clinically used GIs and RMGIs. Further studies are recommended.

How to cite this article

Mousavinasab SM, Khoroushi M, Keshani F, Hashemi S. Flexural Strength and Morphological Characteristics of Resin-modified Glass-ionomer Containing Bioactive Glass. J Contemp Dent Pract 2011;12(1):41-46.


PDF Share
  1. Smart materials in dentistry: Future prospects. Dent Mater J Jan 2009;28(1):37-43.
  2. Smart materials in dentistry. Aust Dent J Jun 2011;56:3-10.
  3. Compressive strength and surface characterization of glass ionomer cements modified by particles of bioactive glass. Dent Mater Mar 2005;21(3):201-09.
  4. Bioactive sol-gel glass added ionomer cement for the regeneration of tooth structure. J Mater Sci Mater Med Oct 2008;19(10):3287-94.
  5. Mechanical properties and microstructures of glass-ionomer cements. Dent Mater Mar 2000;16(2):129-38.
  6. Compound changes and tooth mineralization effects of glass ionomer cements containing bioactive glass (S53P4). An in vivo study. Biomaterials Oct 2005;26(30):5934-41.
  7. Bioactive glass-ionomer cement with potential therapeutic function to dentin capping mineralization. Eur J Oral Sci Oct 2008; 116(5):479-87.
  8. Effects of added bioactive glass on the setting and mechanical properties of resinmodified glass ionomer cement. Biomaterials Aug 2003; 24(18):3061-67.
  9. The Williams dictionary of biomaterials. Liverpool University Press 1996.
  10. The story of bioglass. J Mater Sci Mater Med Nov 2006;17(11):967-78.
  11. Remineralization of human dentin using ultrafine bioactive glass particles. Acta Biomater Nov 2007;3(6):936-43.
  12. Comparative assessment of time-related bioactive glass and calcium hydroxide effects on mechanical properties of human root dentin. Dent Traumatol Feb 2009;25(1):126-29.
  13. Antimicrobial effects of glass ionomer cements containing bioactive glass (S53P4) on oral micro-organisms in vitro. Acta Odontol Scand Aug 2003;61(4):241-46.
  14. Use of bioactive glass in dental filling material. US Patent No. 0065228, 2004.
  15. Effects of incorporation of hydroxyapatite and fluoroapatite nanobioceramics into conventional glass ionomer cements (GIC). Acta Biomater Mar 2008;4(2):432-40.
  16. Release of silica, calcium, phosphorus, and fluoride from glass ionomer cement containing bioactive glass. J Biomater Appl Jul 2004;19(1):5-20.
  17. Sorption and solubility of glass ionomer containing bioactive glass. The IADR/AADR/CADR 85th General Session and Exhibition March 21-24 2007.
  18. Effects of simulated functional loading conditions on dentin, composite, and laminate structures. J Biomed Mater Res B Appl Biomater Feb 2009;88(2):492-501.
  19. Craig's restorative dental materials. (12th ed). St. Louis: Mosby Elsevier 2006;66-68.
  20. Influence of different root canal-filling materials on the mechanical properties of root canal dentin. J Endod Jul 2007;33(7):859-63.
  21. A novel hyperbranched poly(acrylic acid) for improved resin-modified glass-ionomer restoratives. Dent Mater May 2011;27(5):478-86.
  22. Preparation and evaluation of a novel glass-ionomer cement with antibacterial functions. Dent Mater May 2011;27(5):487-96.
  23. Applied dental materials (9th ed). Oxford: Blackwell Publishing Ltd 2008;245-64.
  24. Dental materials and their selection (4th ed). Chicago: Quintessence Publishing Co, In 2008;337-38.
  25. Sturdevant's art and science of operative dentistry (5th ed). St Louis: Mosby Elsevier 2006;150-51.
  26. Structure of bioactive glass and its application to glass ionomer cement. Dent Mater J Jun 1999;18(2):155-66.
PDF Share

© Jaypee Brothers Medical Publishers (P) LTD.