The Effect of 3% Phosphate Ascorbyl Gel on Bond Strength of Composite Resin to Enamel treated with 35% Hydrogen Peroxide
Monica Barros da Silva, Milena de Fátima Schalcher de Castro, Alice Carvalho Silva, Marcela Mayana Pereira Franco, Ana Paula Brito Silva, Fausto da Silva Bramante, Darlon Martins Lima, Adriana de Fátima Vasconcelos Pereira
Citation Information :
da Silva MB, de Castro MD, Silva AC, Franco MM, Silva AP, da Silva Bramante F, Lima DM, Pereira AD. The Effect of 3% Phosphate Ascorbyl Gel on Bond Strength of Composite Resin to Enamel treated with 35% Hydrogen Peroxide. J Contemp Dent Pract 2015; 16 (5):376-382.
To evaluate the effect of 3% phosphate ascorbyl gel (PA) in different times onto the microshear bond strength of composite resin (CR) to bovine enamel treated with 35% hydrogen peroxide (HP).
Materials and methods
Thirty enamel blocks of bovine incisors were made and divided into 5 groups (n = 6) with three specimens per group (n = 18), according to treatment: G1= No bleaching + CR; G2 = HP + CR after 15d; G3 = HP + CR after 24 hours; G4 = HP + PA (15 min) + CR after 24 hours; G5 = HP + PA (2 hours) + CR after 24 hours. The resin cylinders were made by Tygon matrices. Microshear bond strength test was performed using universal testing machine with a 50N load at a speed of 0.5 mm/min. Fracture modes were assessed by a stereomicroscope 40 ×. Microshear bond strength values were submitted to the analysis of variance (ANOVA) one-way and Tukey test (p < 0.05).
Results
G1 had significant results when compared to G3 and G5 (p < 0.01). However, G2, G3, G4 and G5 have showed no significant differences among groups (p > 0.05). Failure modes were categorized into adhesive (90%) and mixed (10%).
Conclusion
The use of 3% phosphate ascorbyl gel for 15 minutes was able to improve bond strength of composite resin to bleached bovine enamel, but when 3% phosphate ascorbyl gel was applied during 40 minutes it negatively interfered in the adhesion of the resin to bleached bovine enamel.
How to cite this article
de Castro MFS, Silva AC, Franco MMP, Silva APB, Bramante FS, da Silva MB, Lima DM, Pereira AFV. The Effect of 3% Phosphate Ascorbyl Gel on Bond Strength of Composite Resin to Enamel treated with 35% Hydrogen Peroxide. J Contemp Dent Pract 2015;16(5):376-382.
Immediate bonding to bleached enamel treated with 10% sodium ascorbate gel: a case report with 1 year follow-up. Eur J Esthet Dent 2012;7(2):154-162.
Antioxidant agents and their effects on shear bond strength of bleached enamel. J Contemp Dent Pract 2013;14(5):871-875.
The effect of hydrogel and solution of sodium ascorbate on bond strength in bleached enamel. Oper Dent 2006;31(4):496-499.
Effect of various antioxidants on the shear bond strength of composite resin to bleached enamel: an in vitro study. J Conserv Dent 2014;17(1):22-26.
The influence of time interval between bleaching and enamel bonding. J Esthet Restor Dent 2007;19(2):111-118.
Reversal of compromised bonding to oxidized etched dentin. J Dent Res 2001;80(10):1919-1924.
Reversal of compromised bonding in bleached enamel. J Dent Res 2002;81(7):477-481.
Reversal of dentin bonding to bleached teeth. Oper Dent 2003;28(6):825-829.
Comparison of the effect of hydrogel and a solution of sodium ascorbate on dentin-composite bond strength after bleaching. J Contemp Dent Pract. 2008;9(2):105-112.
Antioxidant effect on the shear bond strength of composite to bleached bovine dentin. Braz J Oral Sci 2011;10(1):33-36.
Effect of 10% sodium ascorbate on the shear bond strength of composite resin to bleached bovine enamel. J Oral Rehabil 2004;31(12):1184-1191.
Comparison of the effect of hydrogel and a solution of sodium ascorbate on dentin-composite bond strength after bleaching. J Contemp Dent Pract 2008;9(2):105-112.
Effect of nonvital bleaching with 10% carbamide peroxide on sealing ability of resin composite restorations. Int Endod J 2004;37(1):52-60.
Reversal of compromised bonding in bleached enamel using antioxidant gel. Oper Dent 2008;33(4):441-447.
Can the hydrogel form of sodium ascorbate be used to reverse compromised bond strength after bleaching? J Adhes Dent 2009;11(1):35-40.
Effects of 3% sodium ascorbyl phosphate on the hardness and bond strength of human enamel bleached with 10% carbamide peroxide. Gen Dent 2010;58(4):e174-178.
Effect of antioxidant treatment on bond strength of a luting resin to bleached enamel. J Dent 2008;36(10):780-785.
Assessing the use of 35 percent sodium ascorbate for removal of residual hydrogen peroxide after in-office tooth bleaching. J Am Dent Assoc 2011;142(7):836-841.
Effects of 3% sodium ascorbyl phosphate on the hardness and bond strength of human enamel bleached with 10% carbamide peroxide. Gen Dent 2010;58(4):e174-178.
The shear bond strength of acetone and ethanol-based bonding agents to bleached teeth. Pediatr Dent 2006;28(6):531-536.
Effect of sodium ascorbate on the bond strength of silorane and methacrylate composites after vital bleaching. Braz Oral Res 2013;27(4):299-304.
A microshear test to measure bond strengths of dentin-polymer interfaces. Biomaterials 2002;23(17):3603-3608.
Micro-shear bond strength of resin-bonding systems to cervical enamel. Am J Dent 2002;15(6):373-377.
A critical review of the durability of adhesion to tooth tissue: methods and results. J Dent Res 2005;84(2):118-132.
Long-term durability of one-step adhesive-composite systems to enamel and dentin. Oper Dent 2008;33(6):651-657.
Effects of different preparation procedures during tooth whitening on enamel bonding. J Mater Sci Mater Med 2009;20(4):1001-1007.
Influence of time on Bond strength after bleaching with 35% the hydrogen peroxide. J Contemp Dent Pract 2008;9(2):1-8.
Effect of time interval between bleaching and bonding on tag formation. Bull Tokyo Dent Coll 2005;46(1-2):1-6.
Relationship between resin bonding strength and time on deep enamel after bleaching treatment. Zhonghua Kou Qiang Yi Xue Za Zhi 2008;43(6): 360-361.