The Journal of Contemporary Dental Practice

Register      Login

SEARCH WITHIN CONTENT

FIND ARTICLE

Volume / Issue

Online First

Archive
Volume  23 (2022)
Volume  22 (2021)
Volume  21 (2020)
Volume  20 (2019)
Volume  19 (2018)
Volume  18 (2017)
Volume  17 (2016)
Volume  16 (2015)
Volume  15 (2014)
Volume  14 (2013)
Volume  13 (2012)
Volume  12 (2011)
Volume  11 (2010)
Volume  10 (2009)
Volume  9 (2008)
Volume  8 (2007)
Volume  7 (2006)
Volume  6 (2005)
Volume  5 (2004)
Volume  4 (2003)
Volume  3 (2002)
Volume  2 (2001)
Volume  1 (1999)
Related articles

VOLUME 6 , ISSUE 2 ( May, 2005 ) > List of Articles

RESEARCH ARTICLE

The Influence of Some Dentin Primers on Calcium Hydroxide Lining Cement

Alaa El-Araby, Abed Al-Jabab

Citation Information : El-Araby A, Al-Jabab A. The Influence of Some Dentin Primers on Calcium Hydroxide Lining Cement. J Contemp Dent Pract 2005; 6 (2):1-9.

DOI: 10.5005/jcdp-6-2-1

License: CC BY-NC 3.0

Published Online: 01-05-2005

Copyright Statement:  Copyright © 2005; The Author(s).


Abstract

Objective

The purpose of this study was to determine the wear and compressive strength of a calcium hydroxide liner after exposure to different kinds of dentin primers for different periods of time.

Methods

The calcium hydroxide used in this study was Dycal™. It was mixed according to the manufacturer's instructions and placed in plastic rings of 0.5 mm x 5 mm and allowed to set at 37°C for 15 min under 500 gm load. To determine erosion, the height for each sample before and after application of primers was recorded using a Digital Height Measuring Instrument “Digmar” 817. Compressive strength specimens were also prepared.

Results

Calcium hydroxide treated with Optibond (alcohol based) or Syntac (acetone based) for 1 min or 5 min had the highest erosion values and the lowest compressive strength values. Gluma CPs (water based primer) had the least effect on calcium hydroxide values.

Citation

El-Araby A, Al-Jabab A. The Influence of Some Dentin Primers on Calcium Hydroxide Lining Cement. J Contemp Dent Pract 2005 May;(6)2:001-009.

PDF Share
  1. Pulp capping with a new visible-light curing calcium hydroxide composition (Prisma VLC Dycal™), Oper Dent 10:156-163,1985.
  2. Cement bases under amalgam restorations: effect of thickness, Oper Dent 6 (3): 82-89, 1981.
  3. Acid and water solubility and strength of calcium hydroxide bases, J Am Dent Assoc 108: 46-48, 1984.
  4. The effect of enamel etchant on the solubility of three calcium hydroxide bases, J Prosthet Dent 60(2):178-80, 1988.
  5. Weight loss of four calcium hydroxide bases materials following a phosphoric acid etching and washing cycle, J Dent. 14:226-227, 1986.
  6. Comparison of physical properties of commercial calcium hydroxide lining cements, J Am Dent Assoc 107:610-613, 1983.
  7. Resistance of calcium hydroxide preparation to solubility in phosphoric acid, J Prosthet Dent 52:358-360, 1984.
  8. Mixed class V restorations : the potential of a dentin bonding agent, J Dent 18(5): 263-70, 1990.
  9. The effect of composition on erosion properties of calcium hydroxide cements, J Dent Res 61(12): 1431-1435, 1982.
  10. The chemistry of dental cements, Chem Soc Rev. 7:265-296, 1978.
  11. An infrared spectroscopic study of the setting reactions of a calcium hydroxide dental cement, J Mater Sci 14: 2394-2900, 1979.
  12. Disappearing Dycal™ (Letter), Br Dent J 147(5):111, 1979.
  13. Materials for the practicing dentist.
  14. Louis, C.V. Mosby Co., p 32., 1969.
  15. Displacement of cement bases by Amalgam Condensation, J Am Dent Assoc 74:97, 1967.
  16. A comparison of the compressive strength of calcium hydroxide based lining cement, Eur J Prosthodont Restor Dent 3(1): 33-40, 1994.
PDF Share
PDF Share

© Jaypee Brothers Medical Publishers (P) LTD.

We use cookies on this site to enhance your user experience.

By clicking any link on this page you are giving your consent for us to set cookies.